Slickote PTFE 200

Non-Stick, Solid Film Lubricant, Heavy Load

Product Description

Slickote PTFE 200 is a heat cured fluorocarbon-resin bonded solid film lubricant coating with molybdenum disulfide for dry lubrication under heavy loads.

Intended Use

Applied to metal parts to provide a non-stick dry lubricating surface with a low coefficient of friction, particularly under heavy metal to metal loads.

Provides a slick finish.

Excellent corrosion protection for metal surfaces.

Excellent chemical and solvent resistance.

Black only

Application Procedure

Metal Preparation: All surfaces must be thoroughly cleaned, degreased, free of rust, oxides or other surface impurities. Recommended pretreatments:

Aluminum Chemical Conversion Coat or unsealed anodize

Steel Abrasive clean and phosphate coat or acid etch primer

Stainless Steel or Titanium Abrasive Clean

1) Mix well, reduce with Slickote Reducer (or 50/50 MEK and Ethanol ) 2:1 by volume

2) Apply with spray gun , or dip coat

3) Heat cure, 300 deg F for 1 hour

Physical Properties

VOC: <625

Color: Black Semi Gloss

Dilution: 2 parts Slickote Reducer (or 50/50 MEK and Ethanol ) to 1 part base, by volume

Wt/Gal 8.9 Lbs/Gal

%Solids >35%

App.temp: Ambient (< 90 degF)

Cure: 300 deg F for 1 Hour

Shelf Life: 1 year from date of manufacture

Storage: Store in closed container. Store between 32 deg F and 75 deg F