 Slickote® Solid Film Lubricant Coatings

Slickote PTFE100X

PTFE 100 Video
Tech Data Sheet pdf

Product Description

Slickote PTFE 100 is a heat cured fluorocarbon-resin bonded solid film lubricant coating.

Intended Use

Provides a decorative finish for anodized aluminum castings (black- anodized appearance)

Applied to metal parts to provide a non-stick dry lubricating surface with a low coefficient of friction

Provides a slick finish, good for mold release.

Excellent corrosion protection for metal surfaces.

Excellent chemical and solvent resistance.

Provides a decorative finish, in various colors.

Application Procedure

Metal Preparation: All surfaces must be thoroughly cleaned, degreased, free of rust, oxides or other surface impurities. Recommended pretreatments:

Aluminum – Chemical Conversion Coat or unsealed anodize

Steel – Abrasive clean and phosphate coat or acid etch primer

Stainless Steel or Titanium – Abrasive Clean

1) Mix well, mechanical paint shaker

2) Reduce with SlicKote Reducer 2:1

3) Apply with spray gun , or dip coat

4) Heat cure, 300 deg F for 1 hour

Physical Properties

Color: Fed-Std 595 (most colors)

Dilution: Reduce with Acetoner 2:1 by volume

Wt/Gal 8.3 Lbs/gal

App.temp: Ambient (< 90 degF)

Cure: 300 deg F for 1 Hour

Shelf Life: 1 year from date of manufacture

Storage: Store in closed container. Store between 32 deg F and 75 deg F